FY804 PLA granule is a polylactic acid raw material based on lactic acid obtained from corn fermentation. Thanks to its controlled melt flow and low moisture content, it is suitable for use in filament production, sheet, film, and fiber applications.

It is an ideal raw material option, especially for manufacturers aiming for regular feeding, stable extrusion, and consistent product quality in PLA filament production.

Key Features

•⁠  ⁠Product type: PLA granule
•⁠  ⁠Product class: FY804
•⁠  ⁠Appearance: Transparent or semi-transparent granule
•⁠  ⁠Density: 1.24
•⁠  ⁠Moisture content: 0.04%
•⁠  ⁠Melt flow index: 4 g/10 min
    (190 °C / 2.16 kg)
•⁠  ⁠D content: 4%
•⁠  ⁠Typical melting point: 155 °C
•⁠  ⁠Typical glass transition temperature: 60 °C

Areas of Use

•⁠  ⁠3D printer filament production
•⁠  ⁠Sheet and thermoforming applications
•⁠  ⁠Film extrusion
•⁠  ⁠Staple fiber production
•⁠  ⁠Plastic extrusion applications

Batch Quality Values

In the quality control report of the relevant production batch, the moisture content was measured as 0.04%, the melt flow rate as 4.0 g/10 min, the glass transition temperature as 65 °C, and the melting point as 147 °C, indicating that the product complies with the standard.

Packaging and Storage

The product is offered in 25 kg packaging. It should be stored in a cool, dry, and ventilated enclosed area, away from direct sunlight, rain, fire, and moisture. Drying appropriate for the application is recommended before production.